SINTESIS DAN KARAKTERISASI FOTOKATALIS TiO2 MONTMORILONIT TERPILAR ALUMINA

Authors

Iwan Sumarlan , Is Fatimah , Karna Wijaya

DOI:

10.29303/jpm.v11i2.108

Published:

2017-02-22

Issue:

Vol. 11 No. 2 (2016): SEPTEMBER

Articles

Downloads

How to Cite

Sumarlan, I., Fatimah, I., & Wijaya, K. (2017). SINTESIS DAN KARAKTERISASI FOTOKATALIS TiO2 MONTMORILONIT TERPILAR ALUMINA. Jurnal Pijar Mipa, 11(2). https://doi.org/10.29303/jpm.v11i2.108

Downloads

Download data is not yet available.

Metrics

Metrics Loading ...

Abstract

Abstrak. Dispersi TiO2 ke dalam montmorilonit terpilar alumina (PILM) telah sukses dilakukan. Fotokatalis dibuat dengan menginterkalasikan Al13 ke dalam montmorilonit alam kemudian dikalsinasi pada temperatur 500oC. Dispersi TiO2 ke dalam montmorilonit terpilar aluminium (PILM) dilakukan dengan menggunakan metode impregnasi dengan konsentrasi teoritis 0,4; 0,8; 1 dan 3%. Hasil yang diperoleh kemudian dikarakterisasi dengan menggunakan XRD, porosimetry, SEM dan Diffuse Reflectance Spectrophotmetry UV-Visible (DRUV). Hasil karakterisasi fotokatalis Ti/PILM menunjukkan bahwa terjadi penurunan luas permukaan spesifik, volume total pori dan basal spacing setelah dispersi TiO2 pada PILM. Gambar citra SEM menunjukkan bahwa TiO2 masuk ke dalam pori dan juga terdapat pada permukaan fotokatalis. Hasil karakterisasi menggunakan DR UV menunjukkan bahwa band gap fotokatalis Ti/PILM 0,8; 1 dan 3% ialah 3,66; 3,19 dan 3,19 eV.

à

Kata Kunci : Karakterisasi, Montmorilonit, pilarisasi, fotokatalis, TiO2

à


Abstract. Dispersion of TiO2 on montmorillonite pillared aluminium has been done successfully. The photocatalyst were prepared by intercalation of Al13 onto natural montmorillonite and then calcined at 500oC. Titania dispersion onto aluminium pillared montmorillonite was carried out by impregnation method at the theoritic concentration of 0.4, 0.8, 1 and 3% titania. The photocatalyst then characterized by XRD, porosimetry, SEM and Diffuse Reflectance Visible methods. Results of characterization showed that the basal spacing and specific surface area as well as total pore volume were decreased after dispersion of TiO2 on PILM,à meanwhile SEM image exhibited that beside in the pores of PILM, the TiO2 was also dispersed on the surface of PILM. DR UV characterization result indicated that the band gap of TiO2 dispersed PILM for Ti/PILM 0,8%, Ti/PILM 1% and Ti/PILM 3% was 3.66, 3.19 and 3.19 eV respectively

à

Key word : montmorillonite, pillarization, photocatalyst, TiO2

License

The following terms apply to authors who publish in this journal:
1. Authors retain copyright and grant the journal first publication rights, with the work simultaneously licensed under a Creative Commons Attribution License 4.0 International License (CC-BY License) that allows others to share the work with an acknowledgment of the work's authorship and first publication in this journal.

2. Authors may enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., posting it to an institutional repository or publishing it in a book), acknowledging its initial publication in this journal.
3. Before and during the submission process, authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website), as this can lead to productive exchanges as well as earlier and greater citation of published work (See The Effect of Open Access).