Sifat Mekanik Papan Komposit Berbahan Dasar Serat Sabut Kelapa Dan Serat Batang Pisang
DOI:
10.29303/jpft.v3i2.413Diterbitkan:
2017-12-20Terbitan:
Vol 3 No 2 (2017): Juli - DesemberKata Kunci:
composite particle board, coconut fiber, banana fiberArticles
Unduhan
Cara Mengutip
Unduhan
Metrik
Abstrak
Research on the manufacture of composite particle board based on natural fiber: coconut fiber (SSK) and banana fiber (SBP) by using PVAc matrix has been conducted. The purpose of this research is to get the physical and mechanical value of standard on composite board based on SNI03-2105-2006The research method is by taking the comparison of banana fiber reinforcing material (SBP) and coco fiber (SSK) in the form of particle size with composition ie (a) SBP 0%: SKK 100% (b) SBP 50%: SKK 50%, (c) SBP 80%: SSK 20, (d) SBP 60%: SSK 40%, (e) SBP 40%: SSK 60%, (f) SBP 20%: SKK 80%, and (g) SBP 100%: SSK 0%.All composite boards consist of 70 % Matrix and 30% fiber. The result of physical properties for density (ÃÂ) ranges from 0.54 gr / cm3 - 0.75 gr / cm3 and for water content (KA) ranges from 10.5% - 13.9%.As for the mechanical properties of the value of modulus rupture (MOR) ranged between 3483.44 kgf / cm2 - 7472,30 kgf / cm2 and elastic modulus value (MOE) ranged between 15981.23 kgf / cm2 - 27243,74 kgf / cm2. Based on the analysis of tredline graphs, both for physical and mechanical properties, it turns out for each composition of natural fibers to give different values.This means that the composition of the SSK-SBP mixture has an influence on the physical properties as well as the mechanical properties of the composite board. The quality of natural fiber-based composite board (SSK and SBP) both physical and mechanical properties have been in accordance with the standard reference SNI 03-02105-2006.Referensi
Budha, et al. 2011. Pengaruh Alkalisasi Komposit Serat Kelapa-Poliester Terhadap Kekuatan Tarik. Jurnal Rekayasa Mesin. 1(2), 123-129.
Bushra, et al. 2010. Study of the mechanical properties for unsaturated Polyester reinforced by natural fibers. Journal of Al-Nahrain University. 13(3), 65-68.
Clareyna, D.C & Lizda Johar Mawarani. 2013. Pembuatan dan Karakteristik Komposit Poilmer Berpenguat Bagasse. Jurnal Teknik Pomits. 2(2), 208-213.
Ezema, L.C, et al. 2012. Ply Tensile Properties of Banana Stem and Banana Punch Fibers Reinforced Natural Rubber Composite. Nigerian Journal of Technology. 31(1), 25-30.
Khotimah, Khusnul. 2014. Sifat Fisi Komposit Serat batang Pisang sebagai Bahan Penyerap Bunyi. Tesis Magister IPA. Universitas Mataram.
Kartini, R, et al. 2002. Pembuatan dan Karakterisasi Komposit Polimer berpenguat Serat Alam. Jurnal Sains Material Indonesia. 3(3), 30-38.
Kurniawan, E. 2011. Sifat Fisis Polimer Komposit. Tesis. Universitas Mataram
Maleque, M.A., Belal, F.Y., & Sapuan S.M. 2007. Mechanical Properties Study of Pseudo-Stem Banana Fiber Reinforced Epoxy Composite. The Arabian Journal for science and Engineering. 32(2B), 359-364.
Masturi, et al. 2010. Efektivitas Polivinil Acetat Sebagai Matriks pada Komposit Sampah. Jurnal Berkala. 13(2), (61-66)
Multazam, M. 2011. Karakterisasi Papan Komposit Enceng Gondok dengan Matriks Poly Vinil Acetat. Tesis. Universitas Mataram
Oroh, J, et al. 2013. Analisis Sifat Mekanik Material Komposit dari Serat Sabut Kelapa. Universitas Sumatra Utara.
Multazam, M. 2011. Karakterisasi Papan Komposit Enceng Gondok dengan Matriks Poly Vinil Acetat. Tesis. Universitas Mataram.
Nasmi, H. et al. 2011. Analisa Kekuatan Tarik Komposit Termoplastic Diperkuat Serat Pohon Pisang Dengan Arah Serat Searah. Jurnal Teknik Rekayasa. 12(1),-
Noni, N. 2013. Pengaruh Ketebalan Serat Pelepah Pisang Kepok (Musa Paradisiaca) terhadap Sifat Mekanik Material Komposit Poliester-Serat Alam. Jurnal Fisika Unand. 2(3), 195-203.
Nurrani, L. 2012. Pemanfaatan Batang Pisang (Musa sp.) sebagai Bahan Baku Papan Serat dengan Perlakuan Termo-Mekanis. Jurnal Penelitian Hasil Hutan. 30(1), 1-9.
Paryanto, D.S., Sari, N.H. & Putra, D.G.P. 2012. Pengaruh Orientasi dan Fraksi Volume Serat Daun Nanas (Ananas comosus) terhadap Kekuatan Tarik Komposit Polyester Tak Jenuh (UP). Jurnal Dinamika Teknik Mesin, 2(1), 20-32.
Rahayu, M. & Widayani. 2015. Studi Awal Pembuatan Komposit Papan Serar Berbahan Dasar Ampas Sagu. Prosiding SKF. 16-17 Desember 2017.
Rangkuti, Z. 2011. Pembuatan dan karakterisasi papan partikel Dari campuran resin polyester dan serat kulit jagung. Tesis. Universitas Sumatera Utara.
Sudarsono, et al. 2010. Pembuatan Papan Partikel berbahan baku Sabut Kelapa dengan bahan Pengikat Alami (Lem Kopal). Jurnal Teknologi. 3 (1), (22-32)
Wibisono, (2015). Analisa pengujian Tarik Pipa Komposit Serat Batng Pisang Bermatrik Poliester BQTN 157 Dengan Sudut Serat 65o/-65o pada variasi temperature ruang uji. Skripsi. Fak. Teknik. Universitas Muhamadiyah Surakarta.
Lisensi
Penulis yang menerbitkan Jurnal Pendidikan Fisika dan Teknologi (JPFT) setuju dengan ketentuan sebagai berikut:
- Penulis memiliki hak cipta dan memberikan hak jurnal untuk publikasi pertama dengan karya yang dilisensikan secara bersamaan di bawah Lisensi Internasional Creative Commons Attribution-ShareAlike License 4.0 (Lisensi CC-BY-SA). Lisensi ini memungkinkan penulis untuk menggunakan semua artikel, kumpulan data, grafik, dan lampiran dalam aplikasi penambangan data, mesin pencari, situs web, blog, dan platform lain dengan memberikan referensi yang sesuai. Jurnal memungkinkan penulis untuk memegang hak cipta tanpa batasan dan akan mempertahankan hak penerbitan tanpa batasan.
- Penulis dapat membuat pengaturan kontrak tambahan yang terpisah untuk distribusi non-eksklusif dari versi jurnal yang diterbitkan dari karya tersebut (misalnya, mempostingnya ke penyimpanan institusional atau menerbitkannya dalam sebuah buku), dengan pengakuan atas publikasi awalnya di Jurnal Pendidikan Fisika dan Teknologi (JPFT).
- Penulis diizinkan dan didorong untuk memposting karya mereka secara online (misalnya, di repositori institusional atau di situs web mereka) sebelum dan selama proses pengiriman, karena hal itu dapat mengarah pada pertukaran yang produktif, serta kutipan yang lebih awal dan lebih besar dari karya yang diterbitkan (Lihat The Pengaruh Akses Terbuka).