Pembuatan dan Karakterisasi Sifat Fisis Komposit Multilayer Serat Rami
DOI:
10.29303/jpft.v7i2.2783Diterbitkan:
2021-10-23Terbitan:
Vol 7 No 2 (2021): Juli-DesemberKata Kunci:
Multilayer Composites, Physical Properties, Ramie FiberArticles
Unduhan
Cara Mengutip
Unduhan
Metrik
Abstrak
The use of composites as an innovative new material is increasing. Composites are made from two or more materials that have different properties. This research was conducted to make multilayer composites and determine the effect of variations in the number of arrangements and the direction of the fiber angles on the physical properties of composites made from ramie fiber and epoxy. The physical properties of the composites analyzed in this study were density, porosity, water absorption, and thickness expansion. The composites in this study were made using the hand layup method with a volume fraction ratio of 30% and the ratio of epoxy and hardener was 2: 1. Before the composite was made, ramie fibers were soaked in 5% NaOH for 2 hours. This study succeeded in making epoxy ramie multilayer composites with variations in the number of arrangements and the direction of the fiber angles. Variations in the number of layers and the direction angle of the ramie fiber in the composite affect the density and porosity of the composite. Variations in the direction of the ramie fiber in the composite affect the water absorption of the composite. Variations in the number and direction of ramie fiber in the composite did not significantly affect the thickness of the composite.Referensi
Diharjo, K. (2006). Pengaruh Perlakuan Alkali terhadap Sifat Tarik Bahan Komposit Serat Rami-Polyester. Jurusan Teknik Mesin, 8(1), 8ââ¬â13.
Faruk, O., Bledzki, A. K., Fink, H. P., & Sain, M. (2014). Progress Report on Natural Fiber Reinforced Composites. Macromolecular Materials and Engineering, 299(1), 9ââ¬â26. https://doi.org/10.1002/mame.201300008
Firdaus, A. F., Kencanawati, C., & Priambadi, I. G. N. (2019). Pengaruh Variasi Fraksi Volume Serat Kulit Buah Pinang dengan Getah Pinus sebagai Biocomposite terhadap Kekuatan Tarik dan Porositas. Jurnal Ilmiah Teknik Desain Mekanika, 8(2), 529ââ¬â532.
Izaak, F. D., Fentje, A. R., & Romels, L. (2013). Analisis Sifat Mekanik dan Daya Serap Air Material Komposit Serat Rotan. Jurnal Online Poros Teknik Mesin, 2(2).
Kartika, I. A., & Pratiwi, D. F. (2018). Karakteristik Papan Partikel dari Bambu dengan Perekat Getah Damar. Jurnal Teknologi Industri Pertanian, 28(2), 127ââ¬â137. https://doi.org/10.24961/j.tek.ind.pert.2018.28.2.127
Michael, Surya, E., & Halimatuddahliana. (2013). Daya Serap Air dan Kandungan Serat (Fiber Content) Komposit Poliester Tidak Jenuh (Unsaturated Polyester) Berpengisi Serat Tandan Kosong Sawit dan Selulosa. Jurnal Teknik Kimia USU, 2(3), 17ââ¬â21.
Mohammed, L., Ansari, M. N. M., Pua, G., Jawaid, M., & Islam, M. S. (2015). A Review on Natural Fiber Reinforced Polymer Composite and Its Applications. International Journal of Polymer Science, 1ââ¬â15. https://doi.org/10.1155/2015/243947
Mujiono, Nurhadiyanto, D., & Mukhammad, A. F. H. (2017). Ramie Fiber Reinforced Epoxy (RFRE) Composite for Bulletproof Panels. Journal of Fundamental and Applied Sciences, 9(7S), 228ââ¬â240.
Munasir, M. (2011). Studi Pengaruh Orientasi Serat Fiber Glass Searah dan Dua Arah Single Layer terhadap Kekuatan Tarik Bahan Komposit Polypropylene. Journal of Fundamental and Applied Sciences, 1(1), 33ââ¬â41. https://doi.org/10.26740/jpfa.v1n1.p33-41
Muslim, J., Sari, N. H., & Sulistyowati, E. D. (2013). Analisis Sifat Kekuatan Tarik Dan Kekuatan Bending Komposit Hibryd Serat Lidah Mertua Dan Karung Goni Dengan Filler Abu Sekam Padi 5% Bermatrik Epoxy. Dinamika Teknik Mesin, 3(1), 26ââ¬â33.
Naidu, A. L., Jagadeesh, V., & Bahubalendruni, M. V. A. R. (2017). A Review on Chemical and Mechanical Properties of Natural Fiber Reinforced Polymer Composites. International Journal of Advanced Research in Engineering and Technology (IJARET), 8(1), 56ââ¬â68. https://doi.org/10.23940/ijpe.17.02.p8.189200
Nurwahida. (2019). Uji Sifat Mekanik Papan Komposit dari Campuran Serat Batang Pisang dan Serat Kulit Durian Menggunakan Perekan Polyester. Skripsi Fakultas Sains Dan Teknologi Universitas Islam Negeri Alauddin Makasar.
Nuryati, Amalia, R. R., & Hairiyah, N. (2020). Pembuatan Komposit dari Limbah Plastik Polyethylene Terephthalate (PET) Berbasis Serat Alam Daun Pandan Laut (Pandanus Tectorius). Jurnal Agroindustri, 10(2), 107ââ¬â117.
Perdana, D. G. E., Suarsana, K., & Putri, C. I. (2018). Pengaruh Variasi Komposisi Komposit Matrik Aluminium Berpenguat Sicw / Al2O3 dengan Wetting Agent terhadap Densitas , Porositas dan Kekerasan. Jurnal Ilmiah Teknik Desain Mekanika, 7(1), 7ââ¬â12.
Purwanto, D. (2016). Sifat Fisis dan Mekanis Papan Partikel dari Limbah Campuran Serutan Rotan dan Sebuk Kayu. Jurnal Riset Industri, 10(3), 125ââ¬â133.
Reddy, S., & Mandava, R. (2013). Aero Space Applications of GFRP Composites: Reviewââ¬â¢. International Journal of Mechanical Engineering Research, 3, 10ââ¬â14.
Roihan, A., Hartono, R., & Sucipto, T. (2015). Kualitas Papan Partikel Dari Komposisi Partikel Batang Kelapa Sawit Dan Mahoni Dengan Berbagai Variasi Kadar Perekat Phenol Formaldehida. Peronema Forestry Science Journal, 4(2), 10ââ¬â18.
Silalahi, R., Sinuhaji, P., & Simbolon, T. R. (2013). Pembuatan dan Karakterisasi Komposit Serat Kulit Jagung - Poliester dengan Metode Chopped Strand Mat. Saintia Fisika, 4(1), 1ââ¬â5.
Soemardi, T. P., Kusumaningsih, W., & Irawan, A. P. (2009). Karakteristik Mekanik Komposit Lamina Serat Rami Epoksi Sebagai Bahan Alternatif Soket Prostesis. MAKARA of Technology Series, 13(2), 96ââ¬â101. https://doi.org/10.7454/mst.v13i2.487
Wibowo, H., & Ningsih, T. H. (2018). Pengaruh Variasi Arah Serat pada Susunan Lamina Komposit Serat Glass dengan Matrik Polyester terhadap Sifat Mekanik Hasil Pengujian Bending. Jptm, 7(3), 93ââ¬â99.
Biografi Penulis
Naila Hilmiyana Syifa, Universitas Negeri Semarang
Agus Yulianto, Universitas Negeri Semarang
Upik Nurbaiti, Universitas Negeri Semarang
Lisensi
Penulis yang menerbitkan Jurnal Pendidikan Fisika dan Teknologi (JPFT) setuju dengan ketentuan sebagai berikut:
- Penulis memiliki hak cipta dan memberikan hak jurnal untuk publikasi pertama dengan karya yang dilisensikan secara bersamaan di bawah Lisensi Internasional Creative Commons Attribution-ShareAlike License 4.0 (Lisensi CC-BY-SA). Lisensi ini memungkinkan penulis untuk menggunakan semua artikel, kumpulan data, grafik, dan lampiran dalam aplikasi penambangan data, mesin pencari, situs web, blog, dan platform lain dengan memberikan referensi yang sesuai. Jurnal memungkinkan penulis untuk memegang hak cipta tanpa batasan dan akan mempertahankan hak penerbitan tanpa batasan.
- Penulis dapat membuat pengaturan kontrak tambahan yang terpisah untuk distribusi non-eksklusif dari versi jurnal yang diterbitkan dari karya tersebut (misalnya, mempostingnya ke penyimpanan institusional atau menerbitkannya dalam sebuah buku), dengan pengakuan atas publikasi awalnya di Jurnal Pendidikan Fisika dan Teknologi (JPFT).
- Penulis diizinkan dan didorong untuk memposting karya mereka secara online (misalnya, di repositori institusional atau di situs web mereka) sebelum dan selama proses pengiriman, karena hal itu dapat mengarah pada pertukaran yang produktif, serta kutipan yang lebih awal dan lebih besar dari karya yang diterbitkan (Lihat The Pengaruh Akses Terbuka).